A. Rasooli, M. Divandari, H. R. Shahverdi, M. A. Boutorabi. Kinetics and Mechanism of Hydrogen Emission from Titanium Hydride Powder in Air. jame. 2011; 30 (1) :13-24
URL: http://jame.iut.ac.ir/article-1-518-en.html
Faculty of Engineering, Tarbiat Modaress University , ali-rasooli@iust.ac.ir
Abstract:   (6604 Views)
In this research, DTA and TGA curves of titanium hydride powder in air with the heating rates of 5, 10, 20, 25, 30ºC/min were drawn, and XRD patterns of titanium hydride powder during heating rate 10ºC/min were prepared. Results showed that hydrogen comes out of titanium hydride in air during seven stages. And, by increasing heating rate, the mechanism of hydrogen emission from titanium hydride is almost fixed. Upon computation of activation energy of these stages, it was revealed that the mechanism does change at different temperatures. According to DTA curve at 10ºC/min, at temperatures lower than 460ºC, the mechanism is controlled by internal diffusion, at temperatures between 460-650ºC, it is controlled by physicochemical process, and at temperatures higher than 650ºC, it is controlled by chemical reaction. By increasing heating rate, the mechanism is changed at higher temperatures.
Full-Text [PDF 605 kb]   (1330 Downloads)    
Type of Study: Research | Subject: General
Received: 2015/02/9 | Accepted: 2015/05/5 | Published: 2015/05/5

Add your comments about this article : Your username or Email:

Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 CC BY-NC 4.0 | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb