Nikbakht Katouli S, Doostmohammadi A, Esmaeili F. Fabrication of Chitosan/Poly (vinyl alcohol)/Carbon Nanotube/Bioactive Glass Nanocomposite Scaffolds for Neural Tissue Engineering . jame. 2016; 35 (1) :35-46
URL: http://jame.iut.ac.ir/article-1-784-en.html
1- Department of Materials Engineering, Faculty of Engineering, University of Shahrekord, Shahrekord, Iran , alidm14@ma.iut.ac.ir
Abstract:   (12167 Views)

The aim of this study was to fabricate carbon nanotube (CNT) and bioactive glass nanoparticles (BG) (at levels of
5 and 10 wt%) incorporated electrospun chitosan (CS)/polyvinyl alcohol (PVA) nanofibers for potential neural tissue engineering applications.The morphology, structure, and mechanical properties of the formed electrospun fibrous mats were characterized using scanning electron microscopy (SEM) and mechanical testing, respectively. In vitro cell culture of embryonal carcinoma stem cells (P19) were seeded onto the electrospun scaffolds. The results showed that the incorporation of CNTs and BG nanoparticles did not appreciably affect the morphology of the CS/PVA nanofibers. The maximum tensile strength (7.9 MPa) was observed in the composite sample with 5 %wt bioactive glass nanoparticles. The results suggest that BG and CNT-incorporated CS/PVA nanofibrous scaffolds with small diameters, high porosity, and promoted mechanical properties can potentially provide many possibilities for applications in the fields of neural tissue engineering and regenerative medicine.

Full-Text [PDF 3140 kb]   (2574 Downloads)    
Type of Study: Research | Subject: General
Received: 2016/06/14 | Accepted: 2016/06/14 | Published: 2016/06/14

Add your comments about this article : Your username or Email:

Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 CC BY-NC 4.0 | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb