M. Bahrami, M.H. Fathi, M. Ahmadian. Preparation, Characterization and Mechanical Properties Evaluation ofCo-Based Alloy Nanocomposite Reinforced with ForsteriteNanopowder. jame. 2013; 32 (1) :69-78
URL: http://jame.iut.ac.ir/article-1-552-en.html

Biomaterials Group, Department of Materials Engineering, Isfahan University of Technology, Isfahan
Abstract:   (1616 Views)
Short life of current total hip replacement metallic implants is generally dependent on the aseptic loosening of the implant, which occurs due to mismatch of elastic modulus between bone and metallic implant materials. Decreasing in elasticmodulus of implant could be successful. Forsterite is biocompatible and bioactive ceramic which has suitable mechanical properties. In presented research the composite materials based on Co-Cr-Mo alloy with 10, 15 and 20wt% of forsteritenanopowder as reinforcement were fabricated and mechanical behavior of the composites were evaluated. Composites were fabricated by ball milling, cold pressing and sintering. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used for characterization and evaluation phase composition and microstructure of the composites. Density, microhardness, compressive strength and elastic modulus of fabricated composites were evaluated. Obtained results showed elastic modulus of composite materials based on Co-Cr-Mo alloy reinforced with 10, 15 and 20wt% of forsteritenanopowder decreased significantly. Results also showed that the compressive strength of Co-base alloy composites reinforced with 10, 15 and 20 wt% forsterite were lower than cast Co-Cr-Mo alloy. With increasing in the content of reinforcement, compressive strength of the composites were decreased. Microhardness of prepared composites were higher than cast Co-Cr-Mo alloy. With increasing in content of bioceramic reinforcement, microhardness of the composites were increased.
Full-Text [PDF 1230 kb]   (337 Downloads)    
Type of Study: Research | Subject: General
Received: 2015/02/9 | Accepted: 2015/05/6 | Published: 2015/05/6

Add your comments about this article : Your username or email:
Write the security code in the box

Send email to the article author

© 2015 All Rights Reserved | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb