Volume 34, Issue 2 (Journal of Advanced Materials- Summer 2015)                   jame 2015, 34(2): 61-69 | Back to browse issues page

XML Persian Abstract Print

Iran University of Science and Technology, Tehran, Iran , mirkazemi@iust.ac.ir
Abstract:   (8240 Views)
In this investigation, the effect of heat treatment on magnetic properties of glass and nano-structured cobalt-ferrite glass-ceramic was studied. The glass was synthesized in the system of Na2O-Fe2O3-CoO-B2O3-SiO2. Based on DTA results, heat treatment was done at different times and temperatures. X-ray diffraction pattern of glass-ceramic showed the crystallization of CoFe2O4 and some nonmagnetic phases. The highest magnetization of 11.8 emu/g was obtained for the sample heat-treated for 2 hr at 670C in graphite bed. Average crystallite size of CoFe2O4 in this sample was 50 nm. Scanning Electron Microscopy (SEM) confirmed the formation of cobalt ferrite nanoparticles in the glass matrix.
Full-Text [PDF 639 kb]   (3640 Downloads)    
Type of Study: Research | Subject: Surface engineering and coatings
Received: 2015/09/2 | Accepted: 2015/09/2 | Published: 2015/09/2