Hakimi M, Kameli P, Aslibeiki B, Faqeeh A. Preparation of Cobalt Ferrite Nanocrystallites by Annealing of Alloyed Intermetallic Co-Fe and Study of Magnetic Behavior. jame. 2017; 35 (4) :83-89
URL: http://jame.iut.ac.ir/article-1-879-en.html

Abstract:   (740 Views)

In this work, cobalt ferrite nanocrystallites were synthesized by air annealing of milled Co-Fe compound. Effect of annealing temperature on phase formation of cobalt ferrite and structural and magnetic properties of the product was studied. Analysis of annealed sample in 450 oC showed that around 46 weight percent of the specimen was changed to Co2FeO4. This value increased to 95 and 90% for 800 oC and 900 oC annealed samples respectively. Reduction of saturation magnetization under annealing was related to transformation of Co-Fe to cobalt ferrite. Increasing the value of saturation magnetization in 900 oC annealed sample compared to 800 oC one was attributed to decreased surface to volume ratio and crystallite size. The main reason of occurrence of maximum coercivity in 800  oC annealed sample was its low crystallite size.

Full-Text [PDF 490 kb]   (199 Downloads)    
Type of Study: Research | Subject: Welding and joining
Received: 2017/02/19 | Accepted: 2017/02/19 | Published: 2017/02/19

Add your comments about this article : Your username or email:
Write the security code in the box

Send email to the article author

© 2015 All Rights Reserved | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb