دانشگاه صنعتی اصفهان مواد پیشرفته در مهندسی 2251-600X 35 3 2022 12 31 An Investigation of Evolutions during Liquid Phase Sintering of Systems with Volatile Components بررسی تغییرات ایجاد شده در حین تف‌جوشی فاز مایع آلیاژهای حاوی اجزاء تبخیر شونده 95 105 2388 10.18869/acadpub.jame.35.3.95 FA مهرداد موسی پور 1- دانشکده مهندسی مواد، دانشگاه صنعتی سهند تبریز مازیار آزادبه 1- دانشکده مهندسی مواد، دانشگاه صنعتی سهند تبریز احد محمدزاده 2- باشگاه پژوهشگران جوان و نخبگان، دانشگاه آزاد اسلامی، واحد اهر Journal Article 2022 12 31 In this paper, the possibility of elephant foot phenomenon in sintered alloys with volatile components has been studied. To do this, Cu-28Zn brass samples were sintered at the range of 890-970°C for 20 min. The in situ images from brass samples were taken at various sintering conditions. It is concluded that although liquid is pulled down by gravity, but elephant phenomenon was not appeared in these compacts. Instead, the samples were swelled. Chemical composition change and pores coarsening due to zinc evaporation could be considered as the main cause of swelling in brass compacts. هدف از انجام این پژوهش بررسی امکان بروز پدیده پاشنه فیلی در آلیاژهای تف‌جوشی شده حاوی عامل تبخیر شونده است. به این منظور قطعات برنجی با ترکیب Cu-28Zn در محدوده دمایی 890-970 درجه ‌سانتی‌گراد به‌مدت 20 دقیقه تف‌جوشی شدند. از قطعات برنجی در شرایط مختلف تف‌جوشی به­صورت درجا، عکس­برداری شد. نتیجه این­ بود که با وجود کشیده شدن مذاب به سمت نواحی پایین بر اثر نیروی جاذبه زمین، پدیده پاشنه فیلی در این قطعات مشاهده نشد و به جای آن قطعات دچار تورم شدند. تغییر ترکیب شیمیایی و افزایش اندازه حفرات در اثر تبخیر روی را می­توان به عنوان اصلی­ترین عامل بروز این پدیده دانست. https://jame.iut.ac.ir/article_2388_d04863f100d59b3eb688a11f95b0ae60.pdf