M. H. Enayati and M. Salehi. An Investigation of the Use of Ni3Al Intermetallic Compound for Fabrication of Al Matrix Composites. jame. 2007; 25 (2) :183-190
URL: http://jame.iut.ac.ir/article-1-399-en.html
Abstract:   (6517 Views)
Fabrication and characterization of aluminum matrix composites containing different volume fractions of Ni3Al powder (5-40 Vol%) were investigated. Ni3Al powder was produced by mechanical alloying of elemental nickel and aluminum powder mixture. Al-Ni3Al composite parts were prepared using a powder metallurgy route involving two stages Al and Ni3Al powder mixtures were first compacted under 500MPa and then hot-pressed under 250MPa at 420 oC for 10min. The microstructure and hardness of consolidated parts were investigated by x-ray diffractometery, optical and scanning electron microscopy and hardness measurements. Results showed that consolidated Al-Ni3Al samples included no significant porosity with a nearly uniform distribution of Ni3Al particles. Additionally, structural examinations showed that no significant reaction between Ni3Al and aluminum matrix occurred during sintering process. Al-Ni3Al composites exhibited a higher hardness value compared with pure aluminum sample prepared under identical conditions. The hardness value of Al-Ni3Al composites increased linearly as Ni3Al content increased.
Full-Text [PDF 8569 kb]   (1171 Downloads)    
Type of Study: Research | Subject: General
Received: 2014/10/25 | Published: 2007/01/15

Add your comments about this article : Your username or Email:

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 CC BY-NC 4.0 | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb