M. Talebian, M. Alizadeh, M. Ehteshamzadeh. An Investigation of the Effects of Cold Rolling and Annealing on the Corrosion and Tensile Behaviors of Al/Steel Multilayer Composite. jame 2015; 33 (2) :1-15
URL: http://jame.iut.ac.ir/article-1-575-en.html
, milad.talebian@yahoo.com
Abstract:   (10848 Views)
In this study, Al/Steel multilayer composite was produced by accumulative roll bonding (ARB) process using Al-1100 and St-12 strips. Microstructure, mechanical properties and corrosion behavior of the composite were studied by scanning electron microscopy (SEM), tensile test, Vickers microhardness tests, cyclic polarization and electrochemical impedance spectroscopy (EIS) measurement in 3.5 wt% NaCl solution. After one ARB cycle (2 roll-bonding cycles), the multilayer composite of 4 layers of Al and 2 layers of steel was produced. The tensile strength of the Al/steel multilayer composite reached 390.57 MPa after the first ARB cycle, which was 1.29 times larger than that of the starting steel while composite density was almost half the density of the steel. Corrosion behavior of the composite revealed a considerable improvement in the main electrochemical parameters, as a result of enhancing influence of cold rolling. The results indicated that strength and corrosion resistance of Al/steel composite generally decreases and elongation increases after annealing.
Full-Text [PDF 25453 kb]   (4541 Downloads)    
Type of Study: Research | Subject: General
Received: 2015/02/25 | Accepted: 2015/02/25 | Published: 2015/02/25

Add your comments about this article : Your username or Email:

Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 CC BY-NC 4.0 | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb