Volume 39, Issue 4 (Journal of Advanced Materials-Winter 2021)                   jame 2021, 39(4): 23-44 | Back to browse issues page

XML Persian Abstract Print

Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Hosseini S N, Karimzadeh F, Enayati M H. Development of Copper-Ferrite Spinel Coating on AISI 430 Steel Used as Solid Oxide Fuel Cell. jame 2021; 39 (4) :23-44
URL: http://jame.iut.ac.ir/article-1-1033-en.html
1. Department of Mechanical Engineering, Persian Gulf University, Boshehr, Iran. 2. Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran. , n.hosseini@pgu.ac.ir
Abstract:   (2468 Views)
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The results showed that the spinel protection layer not only significantly decreased the area specific resistance (ASR), but also inhibited the subscale growth by acting as a barrier to the inward diffusion of oxygen. ASRs of 19.7 and 32.5 mΩ.cm2, much lower than that of the bare substrate (153.4 mΩ.cm2), at 800 °C after 400 h oxidation were achieved for the bare and pre-oxidized copper ferrite spinel coated samples, respectively. Excellent, stable ASR (20.5 mΩ.cm2) was obtained with copper ferrite coating after 600 h of exposure at 800 °C. The high electrical conductivity of CuFe2O4 and its doping by Mn, the growth reduction of Cr2O3 oxide scale and the good coating to substrate adherence are proposed to be responsible for substantial improvement in electrical conductivity.
Full-Text [PDF 1760 kb]   (415 Downloads)    
Type of Study: Research | Subject: Surface engineering and coatings
Received: 2019/04/22 | Accepted: 2020/12/9 | Published: 2020/12/20

Add your comments about this article : Your username or Email:

Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 CC BY-NC 4.0 | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb