A. Samadi, A. Abdollah-zadeh, S.H. Razavi, H. Assadi. The effect of cooling rate on the precipitation of γ′ in Ni-11.6 at.%Al alloy. jame. 2010; 29 (1) :9-19
URL: http://jame.iut.ac.ir/article-1-507-en.html
Faculty of Materials Engineering, Sahand University of Technology , samadi@sut.ac.ir
Abstract:   (5274 Views)
The initial stages of the  precipitation in a dilute Ni-Al binary alloy, Ni-11.6 at.%Al, were studied using differential scanning calorimetry (DSC), X-ray diffraction (XRD), electron diffraction and electron microscopy (FEG-SEM and TEM) techniques. Three samples were similarly solution treated and then cooled to room temperature under different cooling rates, 170، 25 and 0.03oCs-1. The results indicate a clearly homogenous  nucleation during rapid quenching which takes place via simultaneous ordering and phase separation. However, by decreasing the cooling rate to 25oCs-1 the nucleation mechanism changes to heterogeneous on the preferred nucleation sites. The capability of the mentioned empirical techniques for studying the initial stages of the γ′ is another subject which is studied in this article.
Full-Text [PDF 866 kb]   (1461 Downloads)    
Type of Study: Research | Subject: General
Received: 2015/02/9 | Accepted: 2015/05/5 | Published: 2015/05/5

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2021 CC BY-NC 4.0 | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb