Hajizamani M, Alizadeh M, Jenabali-Jahromi S, Alizadeh A. Synthesis and Characterisation of Al-Zn-Mg /3 wt. %Al2O3 Nanostructured Composite using a Pre-milled Matrix Through Mechanical Alloying. jame. 2017; 36 (2) :1-13
URL: http://jame.iut.ac.ir/article-1-688-en.html

Assistant Professor 1. Department of Metals, Materails Devision, Institute of Science and High Technology and Environmental Sciences, Graduate University Kerman, Iran
Abstract:   (607 Views)

Al-Zn-Mg/3 wt-% Al2O3 nanostructured composite powder was synthesized through Mechanical Alloying (MA). At first, the 7014 alloy matrix constituents were milled in a planetary ball mill for 20 hours. Then, 3 wt.% µ-Al2O3 particles were  added to the pre-milled matrix and the nanostructured composite powder was produced at different MA times to investigate the effects of MA time on the characteristics of the produced composite powders such as morphology, crystallite size, lattice strain and microhardness. The characterization results proved that synthesizing nanostructured composite powder with a low amount of micrometric reinforcements in addition to pre-milled micrometric matrix is possible. Also, synthesis of the nanostructured composite powder with the minimum crystallite size of 24 nm and the minimum mean particle size of 5 µm was confirmed. Moreover, the steady state occurred after around 20 hours milling and further milling did not affect the powder characteristics excluding crystallite size, lattice strain and microhardness. In addition, sinterability of the composite powders increased with increasing the milling time due to decreased average particle size. However, after the steady state, the sinterability did not change.
 
 

Full-Text [PDF 660 kb]   (154 Downloads)    
Type of Study: Research | Subject: Composites
Received: 2015/09/24 | Accepted: 2016/06/29 | Published: 2017/09/4

Add your comments about this article : Your username or Email:
Write the security code in the box

Send email to the article author


© 2015 All Rights Reserved | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb

تحت نظارت وف بومی آسپا-وف