Akbari M, Sabooni S, Enayati M H, Karimzadeh F. Synthesis and Characterization of FeAl/Al2O3 Nanocomposite Coating on Carbon Steel Plate by High Energy Mechanical Alloying. jame. 2017; 36 (2) :107-117
URL: http://jame.iut.ac.ir/article-1-807-en.html

PhD Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Abstract:   (518 Views)

In the present study, FeAl/Al2O3 nanocomposite coating was produced on the carbon steel plate using mechanical alloying (MA) technique via a mechanochemical reaction. Stoichiometric ratios of Fe, Al and Fe2O3 as well as a substrate were mixed and milled up to 22h in a vibrating high energy mill with a 4 mm ball. Samples prepared after 18h of MA were subjected to annealing at 773 K for 1-3 h. X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and microhardness measurements were carried out to study mechanochemical reaction and coating formation characterization. The results showed that mechanochemical reactions were started after 10h of MA, which finally caused the slight formation of FeAl/Al2O3 nanocomposite. Increasing the milling time to 18 hours led to the continuous increase of the coating thickness up to 80 μm, while the coating layer fractured and began to peel by further milling. The microhardness of the coating after 18h milling was 1050 vickers. Annealing of the 18h milled powders at 773K for 3h led to the complete formation and synthesis of the FeAl/Al2O3 nanocomposite. The results showed that the annealing treatment had considerable effects on the hardness increase up to 1200 vickers as well as adhesion strength of the composite coating.
 

Full-Text [PDF 1102 kb]   (127 Downloads)    
Type of Study: Research | Subject: Composites
Received: 2016/08/16 | Accepted: 2017/03/15 | Published: 2017/09/5

Add your comments about this article : Your username or Email:
Write the security code in the box

Send email to the article author


© 2015 All Rights Reserved | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb

تحت نظارت وف بومی آسپا-وف