Effect of Aluminium Injection into the Crystalizator on Type, Composition and Activity of Inclusions in Low Carbon Steel

Authors

Abstract

This study was intended to investigate the effect of injection of aluminium into the crystallizator on type, composition and activity of inclusions in low carbon steel grade USD7. The steel is made in Zob-e-Ahan Isfahan factory and its porosities and inclusions results in the problem of rupturing during rolling process. To improve the quality of this steel, 2.4 mm diameter pure aluminum wires were injected in to the crystallizator at the rate of 2, 4, 6 or 8 m/min in certain periods and then sampling was done. The results indicated that much of the added aluminum changed to aluminum oxide slag, and the remaining part altered the chemical composition of the inclusions. Increased aluminum caused an increase in the activity of alumina and reduction in the activity of other oxides in the slag and existing inclusions in the melt. By increasing Al2O3 activity from 0.313 to 0.649, the Al2O3 formation and oxygen exclusion probability increased in the system. Scanning electron microscopy showed that without aluminium injection, most of inclusions were FeO-MnO type placed around existing porosities in the ingot. The optimum rate of aluminum injection was found to be 4 m/min.

Keywords

References

1. Kudrin V., Steel Making, pp. 101-105Mir Publishers,
Moscow, 1981. 2. Ghosh A., Principles of Secondary Processing and
Casting of Liquid Steel, pp. 134-138, Oxford & IBH
Publishing Co. Pvt. Ltd, India, 1990. 3. Larsen G.G., "The Role and Use of Aluminum in Steel
Production", Ferroalloys and other Additives to
Liquid Iron and Steel, ASTM-STP-739, American
Society for Testing and Materials, pp.151-156, 1981. 4. Turkdogan E.T., “Deoxidation of Steel”, ISIJ
International, pp. 21-36, 1972. 5. Nicholson A. and Gladman T., "Non-Metallic
Inclusions and Developments in Secondary
Steelmaking", Ironmaking and steelmaking, Vol. 13, No. 2, pp. 53-69, 1986. 6. Van Valack L.H., "Oxide Inclusions in Steel: Part D
(A. Gittins: Effect of Oxygen on Hot Workability of
Steel)", International Metals Reviews, Vol. 22, pp. 187-228, 1977. 7. Thomson T.R. and Brownrig A., "The Effect of
Inclusions on Cold Formability”, Metals Forum, Vol. 2, No. 2, pp. 118-125, 1979. 8. Ohta H. and Suito H., "Activities in CaO-SiO2-Al2O3
Slags and Deoxidation Equilibria of Si and Al",
Metallurgical and Materials Transactions, Vol. 27B, pp. 943-950, 1996. 9. Elliott J.F., Physical Chemistry of High Temperature
Reactions, Iron and Steel Society, pp. 265-290, 1985. 10. Gaskell D.R., Introduction to Metallurgical
Thermodynamics, 2
nd Ed., Mc Graw-Hill,1981, 310-pp291, WashingtonYork New,
12. Grigoryan V., Belyanchikov L. and Stomakhin A., Theoretical Principles of Electric Steel Making, Mir
Publishers, Moscow, pp. 50-146, 1979. 13. DIN standards, “Microscopic Examination of Special
Steels Using Standard Diagrams to Assess the
Content of Non-Metallic Inclusion”, DIN-50602, 1985